| ABXV | BORE DIAMETER | 0.2495 INCHES MINIMUM AND 0.2500 INCHES MAXIMUM |
| AGGF | OUTER MEMBER OUTSIDE DIAMETER | 0.6557 INCHES MINIMUM AND 0.6562 INCHES MAXIMUM |
| AGGH | OUTER MEMBER WIDTH | 0.245 INCHES MINIMUM AND 0.255 INCHES MAXIMUM |
| AGGJ | INNER MEMBER WIDTH | 0.341 INCHES MINIMUM AND 0.343 INCHES MAXIMUM |
| AGKP | STATIC RADIAL LOAD RATING | 6040 POUNDS |
| CQFM | HARDNESS RATING | 28.0 ROCKWELL C MINIMUM AND 37.0 ROCKWELL C MAXIMUM OUTER RACE MEMBER |
| CQFM | HARDNESS RATING | 43.0 ROCKWELL C MINIMUM INNER MEMBER |
| CTLM | LUBRICATION FEATURE | SELF-LUBRICATING LINER RACE LINER |
| CXCY | PART NAME ASSIGNED BY CONTROLLING AGENCY | BEARING, PLAIN, SELF-LUBRICATING, SELF-ALIGNING, LOW SPEED, NARROW, CHAMFERED RACE, -65 TO +325 F |
| FEAT | SPECIAL FEATURES | C = PH13-8 BALL MATERIAL. ABSENCE OF THE LETTER A = TESTED TO 25000 CYCLES. P = ZINC-NICKEL OR CADMIUM PLATING. MATERIAL - BALL:PH13-8 CRES PER AMS5629 H1000. RACE: 17-4PH CRES PER AMS5643. LINER: PTFE SHALL BE INCLUDED IN THE LINER. HARNESS RATING IS BEFORE SWAGING. FINISH: RACE: PLATING, WHEN SPECIFIED, SHALL BE ZINC-NICKEL PLATING PER AMS2417, TYPE 2, GRADE B OR CADMIUM PLATING PER AMS-QQ-P-416, TYPE II, CLASS 2. PLATING SHALL BE ON THE OUTSIDE DIAMETER SURFACE AND ON THE FLATS BETWEEN THE OUTSIDE DIAMETER AND THE V-GROOVES. THE PLATING RUNOUT SHALL OCCUR EITHER IN THE V-GROOVES OR ON THE SIDE FACE AREAS BETWEEN THE V-GROOVES AND THE BALL. BALL: PASSIVATE PER AMS2700, METHOD 1 (NITRIC ACID) OR METHOD 2 (CITRIC ACID), OR ASTM A967. CITRIC 1, CITRIC 2, AND CITRIC 3 ARE ACCEPTABLE. (AMS2700, METHOD 1, TYPE 8 IS PROHIBITED ON BEARINGS MANUFACTURED WITH 440C AFTER JUNE 1, 2018). |
| MATT | MATERIAL | PLASTIC POLYTETRAFLUOROETHYLENE RACE LINER |
| MATT | MATERIAL | STEEL CORROSION RESISTING INNER MEMBER |
| MATT | MATERIAL | STEEL CORROSION RESISTING OUTER RACE MEMBER |
| MDCL | MATERIAL DOCUMENT AND CLASSIFICATION | AMS5629 H1000 INTERNATIONAL STD/SPEC ALL MATERIAL RESPONSES INNER MEMBER |
| MDCL | MATERIAL DOCUMENT AND CLASSIFICATION | AMS5643 INTERNATIONAL STD/SPEC ALL MATERIAL RESPONSES OUTER RACE MEMBER |
| SFTT | SURFACE TREATMENT | CADMIUM OR ZINC OR NICKEL ALLOY INNER MEMBER |
| SFTT | SURFACE TREATMENT | PASSIVATE OUTER RACE MEMBER |
| STDC | SURFACE TREATMENT DOCUMENT AND CLASSIFICATION | AMS2417, TYPE 2, GRADE B INTERNATIONAL STD/SPEC ALL TREATMENT RESPONSES OR AMS-QQ-P-416, TYPE II, CLASS 2 INTERNATIONAL STD/SPEC ALL TREATMENT RESPONSES INNER MEMBER |
| STDC | SURFACE TREATMENT DOCUMENT AND CLASSIFICATION | AMS2700, METHOD 1 (NITRIC ACID) OR METHOD 2 (CITRIC ACID) INTERNATIONAL STD/SPEC ALL TREATMENT RESPONSES OR ASTM A967. CITRIC 1, CITRIC 2, AND CITRIC 3 INTERNATIONAL STD/SPEC ALL TREATMENT RESPONSES OUTER RACE MEMBER |
| STYL | STYLE DESIGNATOR | WITH INSERT AND/OR LINER WITH STAKING GROOVE |